KORODUR 04
for KORODUR Hard Aggregate Industrial Floors
DESCRIPTION
KORODUR 0/4 – hard aggregate acc. to DIN 1100 - A 0/4 KORODUR 0/4 – mineral hard aggregate produced from high grade components including quartz sand and tough by-products of electrometallurgical melting processes.
This special mixture guarantees outstanding tensile and compressive strength values, very favourable wearing properties and imparts stable anti-skid properties to industrial flooring surfaces.
APPLICATION
For use in hard aggregate concrete screeds acc. to DIN 18 560, ZE 65 A. For use in areas of combined rolling, ramming and grinding stress, percussion, pressure and impact. Able to withstand the sliding and rolling of work parts, plant traffic of all kinds, fork-lift traffic, crawler tractor traffic and transporting equipment with steel wheels etc.
Especially qualified for wet rooms, parking areas, driving and loading ramps, bunker linings and outdoor surfaces of all kinds.
PROPERTIES
• resistant to gasoline, mineral oil,solvents
• highly wear resistant even under the most severe stress
• fork lift-truck resistant
• water-resistant, qualified for wet rooms
• anti-skid, non-slip in wet rooms
• frost and de-icer resistant
• non-rusting
• electrostatic non-chargeable
• high surface density
• physiological and ecological harmless
• easy to clean
Certification: DIN EN ISO 9001:200
HARD AGGREGATE COATING GROUP A DIN 1100
|
| standard resp. characteristic values of the hard aggregate acc. to DIN 1100 | standard values acc. to DIN 18560-7 resp. EN 13813 |
|
| coating group A | e.g. hard aggregate screed DIN 18560-CT-C 70-F 10-A 5-DIN 1100-A |
| tensile strength [N/mm2] | 10** | 10*
|
| compressive strength [N/mm2] | 80** | 70* |
| wear*** [cm3/50 cm2] | <= 5* | 5* |
| bulk density* [kg/dm3] | acc. to DIN 1100 | |
| granulometric composition* | acc. to DIN 1100 | |
* standard values ** characteristic values *** average value
KORODUR 0/4 meets all demands according to factory and outside control
GROUPS OF MECHANICAL STRESS DIN 18 560, Part 7, Table 1
| Stress group | mobile industrial handling equipment, kind of tires 1) | operational processes and pedestrian traffic |
| I (heavy) | steel and polyamide | processing, sliding and rolling of metal parts, placing down of goods by means of metal forks, pedestrian traffic of more than 1.000 persons/day |
| II (medium) | urethane-elastomer and rubber | sliding and rolling of wood, paper rolls and plastic castings, pedestrian traffic of 100 to 1.000 persons/day |
| III (light) | solid tires and pneumatic tires | assembly areas (on tables), pedestrian traffic up to 100 persons/day |
| 1) refers only to clean tires. Pressed in grit and dirt on tires increase the stress. | ||
Remarks:
Where loading and abrasion potential is beyond the guidelines for „Stress group I“, e.g. assembly of heaviest equipment or traffic of heaviest vehicles (crawlers) special precautionary measures must be taken.
PROCESSING / CONSUMPTION KORODUR 0/4
| Stress group acc. to DIN 18560, Part 7, Table 1 | Topping thickness acc. to DIN 18560, Part 7, Table 1, nominal thicknesses | Mixing ratio indoor surfaces: 1 weight unit cement: 2 weight units KORODUR 0/4 |
| I (heavy) II (medium) III (light) | 15 mm 10 mm 8 mm | 21 kg/1 m² KORODUR 0/4 14 kg/1 m² KORODUR 0/4 12 kg/1 m² KORODUR 0/4 |
We recommend:
KOROTEX for after-treatment, KOROPOX for impregnation.